PT Journal
AU Kucera, V
   Prusa, F
   Vojtech, D
TI Processing of Al-Fe Scraps by Powder Metallurgy
SO Manufacturing Technology Journal
PY 2016
BP 726
EP 732
VL 16
IS 4
DI 10.21062/ujep/x.2016/a/1213-2489/MT/16/4/726
DE AlFe alloy; centrifugal atomization; spark plasma sintering; hot extrusion
AB Iron has a low solubility in aluminium solid solution even at elevated temperatures and forms brittle intermetallic phases with needle-like or platelets-like morphology when it is produced by conventional casting technologies. These phases have a detrimental effect on mechanical properties. Therefore with increasing significance of recycling and also amount of aluminium scrap that needs to be recycled, it is necessary to find a promising ways of processing such waste materials. Powder metalurgy leads to intensive microstructural refinement, increases solid solubility of alloying elements and overall to improvement of mechanical properties. Hence, it belongs to promising alternatives for proccesing aluminium materials with increased amount of iron. Aluminium alloy with 17 wt. % iron was prepared by centrifugal atomization and consolidated by spark plasma sintering followed by hot extrusion. The microstructure and phase composition of compact samples as well as mechanical properties were studied. Fine microstructure has been achieved by centrifugal atomization and consolidation by spark plasma sintering in combination with hot extrusion. Compression strength was 565 MPa with remarkable ductility reaching almost 35 %.
ER